Popular PF, traditional red earth clay, has been adapted for 3D printing.
It is a high-quality and highly valuable clay, very popular for its fineness and plasticity.
Thermal expansion coefficients are ideal for standard ceramic glazes in both single and double firing processes.
Available in extruded body with ideal moisture content for 3D printing.
Presented in a practical cylindrical format with double packaging.
Firing range: 970-1055ºC
Water content (extrusion): 25% Plasticity (IP Atterberg): 17
Carbonate content (CaCO3): 10% Drying shrinkage: ≈7%
Firing shrinkage (1000ºC): 0.6%
Porosity (water absorption at 1000ºC): 13.5%
Dry flexural strength: 6.6 N/ mm2
Fired flexural strength (1000ºC): 27.9 N/mm2
Thermal coefficient (25-500ºC): 77.7x10^-7ºC^-
Available in 5kg packages.